PMC-hard rubbers

PMC-Series

These are somewhat harder PU-rubbers that are traditionally used in the ceramic industry.
They exhibit excellent wear resistance, cure with negligible shrinkage and are economical.

Technical bulletin PMC 744
Technical bulletin PMC 746
Technical bulletin PMC 770
Technical bulletin PMC 780
Technical bulletin PMC 790

PMC Series

hardness:

44A 60A 70A 80A 90A

size relative:

Medium Small

PMC-780 Wet /1,35kg
PMC-780 is a hard pourable rubber with exceptional mechanical properties. High abrasion resistance. Shore 80. Wet version WITH build-in release agent. set 1,35 kg
31.60 €*
PMC® 746 /1,36 kg
PMC® 746 developed to make molds for casting gypsum plasters. This product is well suited for use as a rubber case mold. Shore hardness is A60. Durable and moisture resistant. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
33.90 €*
PMC® 746 /10,89 kg
PMC® 746 developed to make molds for casting gypsum plasters. This product is well suited for use as a rubber case mold. Shore hardness is A60. Durable and moisture resistant. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
213.25 €*
PMC™-744 /1,36 kg
PMC™-744 has been used for years by mold making professionals to cast plaster, concrete, resins, etc. It is excellent for making molds that are strong, durable and dimensionally stable. Low viscosity ensures fine detail reproduction. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
35.00 €*
PMC™-744 /10,89 kg
PMC™-744 has been used for years by mold making professionals to cast plaster, concrete, resins, etc. It is excellent for making molds that are strong, durable and dimensionally stable. Low viscosity ensures fine detail reproduction. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
212.95 €*
PMC™-770 /1,36 kg
PMC™-770 is a Shore 70A liquid urethane rubber used for a variety of industrial and casting applications. Mix ratio is 2A;1B, pot life is 30 minutes, cure time is 16 hours.
33.95 €*
PMC™-770 /10,89 kg
PMC™-770 is a Shore 70A liquid urethane rubber used for a variety of industrial and casting applications. Mix ratio is 2A;1B, pot life is 30 minutes, cure time is 16 hours.
248.15 €*
PMC™-780 Dry /1,36 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. Original PMC™-780 Dry does not exude oil. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
31.60 €*
PMC™-780 Dry /10,89 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. Original PMC™-780 Dry does not exude oil. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
223.30 €*
PMC™-780 Wet /10,89 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC™-780 Wet extrudes an oil that acts as a release agent. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
223.30 €*
PMC™-790 /1,36 kg
PMC™-790 is a Shore 90A industrial urethane rubber compound designed to meet the most stringent requirements of industrial production applications. It is a very hard rubber that offers superior tear and tensile strength as well as impact and abrasion resistance. Mix ratio 2A:1B, pot life 20 minutes, cure time 48 hours.
34.10 €*
PMC™-790 /10,89 kg
PMC™-790 is a Shore 90A industrial urethane rubber compound designed to meet the most stringent requirements of industrial production applications. It is a very hard rubber that offers superior tear and tensile strength as well as impact and abrasion resistance. Mix ratio 2A:1B, pot life 20 minutes, cure time 48 hours.
242.10 €*

No products were found that match your selection criteria.

* All prices exclusive VAT exclusive shipping

PMC Series_

hardness:

44A 60A 70A 80A 90A

size relative:

Medium Small

PMC-780 Wet /1,35kg
PMC-780 is a hard pourable rubber with exceptional mechanical properties. High abrasion resistance. Shore 80. Wet version WITH build-in release agent. set 1,35 kg
31.60 €*
PMC® 746 /1,36 kg
PMC® 746 developed to make molds for casting gypsum plasters. This product is well suited for use as a rubber case mold. Shore hardness is A60. Durable and moisture resistant. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
33.90 €*
PMC® 746 /10,89 kg
PMC® 746 developed to make molds for casting gypsum plasters. This product is well suited for use as a rubber case mold. Shore hardness is A60. Durable and moisture resistant. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
213.25 €*
PMC™-744 /1,36 kg
PMC™-744 has been used for years by mold making professionals to cast plaster, concrete, resins, etc. It is excellent for making molds that are strong, durable and dimensionally stable. Low viscosity ensures fine detail reproduction. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
35.00 €*
PMC™-744 /10,89 kg
PMC™-744 has been used for years by mold making professionals to cast plaster, concrete, resins, etc. It is excellent for making molds that are strong, durable and dimensionally stable. Low viscosity ensures fine detail reproduction. Mix ratio 2A:1B, pot life 15 minutes, cure time 16 hours.
212.95 €*
PMC™-770 /1,36 kg
PMC™-770 is a Shore 70A liquid urethane rubber used for a variety of industrial and casting applications. Mix ratio is 2A;1B, pot life is 30 minutes, cure time is 16 hours.
33.95 €*
PMC™-770 /10,89 kg
PMC™-770 is a Shore 70A liquid urethane rubber used for a variety of industrial and casting applications. Mix ratio is 2A;1B, pot life is 30 minutes, cure time is 16 hours.
248.15 €*
PMC™-780 Dry /1,36 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. Original PMC™-780 Dry does not exude oil. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
31.60 €*
PMC™-780 Dry /10,89 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. Original PMC™-780 Dry does not exude oil. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
223.30 €*
PMC™-780 Wet /10,89 kg
PMC™-780 is a premium shore 80A performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC™-780 Wet extrudes an oil that acts as a release agent. Mix ratio is 2A:1B, pot life is 25 minutes, cure time is 48 hours.
223.30 €*
PMC™-790 /1,36 kg
PMC™-790 is a Shore 90A industrial urethane rubber compound designed to meet the most stringent requirements of industrial production applications. It is a very hard rubber that offers superior tear and tensile strength as well as impact and abrasion resistance. Mix ratio 2A:1B, pot life 20 minutes, cure time 48 hours.
34.10 €*
PMC™-790 /10,89 kg
PMC™-790 is a Shore 90A industrial urethane rubber compound designed to meet the most stringent requirements of industrial production applications. It is a very hard rubber that offers superior tear and tensile strength as well as impact and abrasion resistance. Mix ratio 2A:1B, pot life 20 minutes, cure time 48 hours.
242.10 €*

No products were found that match your selection criteria.

* All prices exclusive VAT exclusive shipping

Technical information
Table
Instructions

PMC-744 info

PMC-744 has been used for years by mold making professionals to cast plaster, concrete, resins, etc. It is excellent for making molds that are strong, durable and dimensionally stable. Low viscosity ensures fine detail reproduction.

PMC-744 is ideal for making ceramic case molds and plaster block molds, reproducing ornamental plaster, making molds for casting concrete, casting a variety of Smooth-On urethane resins, casting wax and making a variety of mechanical rubber parts.

- Semi Transparent Amber Colour
- Shore 44A

Technical Bulletin

PMC-746 info

PMC-746 was developed to make molds for casting gypsum plasters. It is well suited for use as a rubber case mold especially large case molds where extra rigidity is required. Durability and moisture resistant properties PMC-746 is also used by zoos and museums for a variety of mold-making, display and exhibit applications. Other applications include making plaster block molds, reproducing ornamental plaster, pre-cast concrete molds, casting waxes, rigid polyurethanes, epoxies and a variety of special effects.

Shore hardness is 60 A
mix ratio: 2:1 by weight or volume
contains no mercury.

Technical Bulletin

PMC-770

Shore 70A rubber that has exceptional dimensional stability. It is suitable for production casting of abrasive materials such as concrete (pre-cast concrete, making concrete stamping pads, etc.) and gypsum plasters with high exotherms. Suitable for rubber mechanical parts of varying configurations (gaskets, wheels, pulleys) as well as ball mill liners and vibration/shock pads.

Shore 70A hardness
mixed two parts A to one part B by weight

PMC-780 WET

bnzbnbnbfnbnbasd

PMC-780 Wet contains a built-in release agent to aid in demolding concrete. Both are used around the world for casting abrasive materials such as concrete (pre-cast concrete, making concrete stamping pads, etc.) and gypsum plasters with high exotherms.

PMC -780 is a premium performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC -780 Dry does not exude an oil.

Shore 80A hardness
mixed two parts A to one part B by weight
negligible shrinkage

PMC-780 DRY

bnzbnbnbfnbnbasd

PMC -780 Dry is also commonly used to make rubber mechanical parts of varying configurations (gaskets, wheels, pulleys) as well as ball mill liners and vibration/shock pads. PMC -780 Dry does not exude an oil.

PMC -780 is a premium performance urethane rubber that offers exceptional strength, durability and abrasion resistance.

Shore 80A hardness
mixed two parts A to one part B by weight
negligible shrinkage

PMC-790

PMC -790 Urethane Rubber - PMC -790 is an industrial urethane rubber compound designed to meet the most stringent requirements of industrial production applications. It is a very hard rubber that offers superior tear and tensile strength as well as impact and abrasion resistance. PMC -790 is suitable for a variety of industrial applications including making concrete stamping pads, mold liners and molds for casting concrete. PMC -790 is also good for making ball mill liners, industrial rollers and belts, rubber mechanical parts.

Shore 90A hardness

PMC Properties Table

PMC	A:B mixing ratio	Demold Time	Elongation at Break	Mixed Viscosity	Pot Life	Shore A Hardness	Tear Strength	Specific Gravity kg/lt
744	2:1 weight/ volume	16 hrs	400 %	3400 cps	15 min	44 A	90 pli	1,000
746	2:1 weight/ volume	16 hrs	650 %	1200 cps	15 min	60 A	100 pli	1,000
770	2:1 by weight	16 hrs	600%	3000 cps	35 min	70 A	160 pli	1,015
780	2:1 weight/ volume	48 hrs	700%	2000 cps	25 min	80 A	200 pli	1,015
790	2:1 weight/ volume	48 hrs	600 %	3000 cps	20 min	90 A	300 pli	1,068

Preparation - Materials should be stored and used in at room (73 F/23 C). Humidity should be low. These products have a limited shelf life and should be used as soon as possible. Wear safety glasses, long sleeves and rubber gloves to minimize contamination risk. Good ventilation (room size) is necessary.

Some Materials Must Be Sealed - To prevent adhesion between the rubber and model surface, models made of porous materials (gypsum plasters, concrete, wood, stone, etc.) must be sealed prior to applying a release agent. SuperSeal or One Step (available from Smooth-On) are fast drying sealers suitable for sealing porous surfaces without interfering with surface detail. Shellac is suitable for rough contours. A high quality Shellac is suitable for sealing modeling clays that contain sulfur or moisture (water based). Thermoplastics (polystyrene) must also be sealed with shellac or PVA.

In all cases, the sealing agent should be applied and allowed to completely dry prior to applying a release agent.

Non-Porous Surfaces - Metal, glass, hard plastics, sulfur free clays, etc. require only a release agent.

Applying A Release Agent - A release agent is necessary to facilitate demolding when casting into or over most surfaces. Use a release agent made specifically for mold making (Universal Mold Release). A liberal coat of release agent should be applied onto all surfaces that will contact the rubber.

IMPORTANT: To ensure thorough coverage, lightly brush the release agent with a soft brush over all surfaces of the model. Follow with a light mist coating and let dry for 30 minutes.

Because no two applications are quite the same, a small test application to determine suitability for your project is recommended if performance of this material is in question.

IMPORTANT: Shelf life of product is reduced after opening. Remaining product should be used as soon as possible. Immediately replacing the lids on both containers after dispensing product will help prolong the shelf life of the unused product. XTEND-IT Dry Gas Blanket (available from Smooth-On) will significantly prolong the shelf life of unused liquid urethane products.

MEASURING & MIXING - Liquid urethanes are moisture sensitive and will absorb atmospheric moisture. Mixing tools and containers should be clean and made of metal, glass or plastic. Materials should be stored and used in a warm environment (73 F/23 C).

IMPORTANT: Pre Mix the Part B before using. After dispensing equal amounts of Parts A and B into mixing container, mix thoroughly for at least 3 minutes making sure that you scrape the sides and bottom of the mixing container several times.

If Mixing Large Quantities (16 lbs./7 kg. or more) at one time, use a mechanical mixer (i.e. Squirrel Mixer or equal) for 3 minutes followed by careful hand mixing for one minute as directed above. Then, pour entire quantity into a new, clean mixing container and do it all over again.

Although this product is formulated to minimize air bubbles in the cured rubber, vacuum degassing will further reduce entrapped air. A pressure casting technique using a pressure chamber can yield totally bubble free castings. Contact Smooth-On or your distributor for further information about vacuum degassing or pressure casting.

Pouring - For best results, pour your mixture in a single spot at the lowest point of the containment field. Let the rubber seek its level up and over the model. A uniform flow will help minimize entrapped air. The liquid rubber should level off at least 1/2 (1.3 cm) over the highest point of the model surface.

Curing - Allow rubber to cure overnight (at least 16 hours) at room temperature (73 F/23 C) before demolding. Cure time can be reduced with mild heat or by adding Smooth-On "Kick-It Cure Accelerator. Do not cure rubber where temperature is less than 65 F/18 C.

Post Curing - After rubber has cured at room temperature, heating the rubber to 150 F (65 C) for 4 to 8 hours will increase physical properties and performance.

Using The Mold - If using as a mold material, a release agent should be applied to the mold before each casting. The type of release agent to use depends on the material being cast. The proper release agent for wax, liquid rubber or thermosetting materials (i.e. Smooth-On liquid plastics) is a spray release made specifically for mold making (available from Smooth-On or your distributor). Prior to casting gypsum plaster materials, sponge the mold with a soap solution for better plaster flow and easy release. In & Out II Water Based Release Concentrate (available from Smooth-On) is recommended for releasing abrasive materials like concrete.

Performance & Storage - Fully cured rubber is tough, durable and will perform if properly used and stored. The physical life of the rubber depends on how you use it. Shrinkage will be higher with wet vs. dry rubbers. Contact Smooth-On directly with questions about this material relative to your application.

PMC-770/780/790 data

PMC	A:B mixing ratio	Demold Time	Elongation at Break	Mixed Viscosity	Pot Life	Shore A Hardness	Tear Strength	Specific Gravity kg/lt
770	2:1 by weight	16 hrs	600%	3000 cps	35 min	70 A	160 pli	1,015
780	2:1 weight / volume	48 hrs	700%	2000 cps	25 min	80 A	200 pli	1,015
790	2:1 weight / volume	48 hrs	600%	3000 cps	20 min	90 A	300 pli	1,068

Guide

Let us help you find your way.

The list below may help you find what you are looking for via an alternative path.